Tensile Stress, yld, Type I, 50 mm/min

630

kgf/cm2

ASTM D 638

Tensile Stress, brk, Type I, 50 mm/min

660

kgf/cm2

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

>70

%

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

940

kgf/cm2

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

23800

kgf/cm2

ASTM D 790

Izod Impact, unnotched, 23°C

NB

cm-kgf/cm

ASTM D 4812

Izod Impact, notched, 23°C

92

cm-kgf/cm

ASTM D 256

Instrumented Impact Energy @ peak, 23°C

652

cm-kgf

ASTM D 3763

Vicat Softening Temp, Rate B/50

154

°C

ASTM D 1525

HDT, 0.45 MPa, 6.4 mm, unannealed

137

°C

ASTM D 648

HDT, 1.82 MPa, 6.4 mm, unannealed

132

°C

ASTM D 648

CTE, -40°C to 95°C, flow

6.84E-05

1/°C

ASTM E 831

Specific Heat

1.25

J/g-°C

ASTM C 351

Specific Gravity

1.2

-

ASTM D 792

Density

1.19

g/cm3

ASTM D 792

Water Absorption, equilibrium, 23C

0.35

%

ASTM D 570

Water Absorption, equilibrium, 100°C

0.58

%

ASTM D 570

Mold Shrinkage, flow, 3.2 mm (5)

0.5 - 0.7

%

SABIC Method

Melt Flow Rate, 300°C/1.2 kgf

3.5

g/10 min

ASTM D 1238

Light Transmission, 2.54 mm

88

%

ASTM D 1003

Haze, 2.54 mm

1

%

ASTM D 1003