Tensile Stress, yld, Type I, 50 mm/min

630

kgf/cm2

ASTM D 638

Tensile Stress, brk, Type I, 50 mm/min

660

kgf/cm2

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min

7

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

110

%

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

940

kgf/cm2

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

23900

kgf/cm2

ASTM D 790

Hardness, Rockwell M

70

-

ASTM D 785

Hardness, Rockwell R

118

-

ASTM D 785

Taber Abrasion, CS-17, 1 kg

10

mg/1000cy

ASTM D 1044

Izod Impact, unnotched, 23°C

326

cm-kgf/cm

ASTM D 4812

Izod Impact, notched, 23°C

92

cm-kgf/cm

ASTM D 256

Tensile Impact, Type S

557

cm-kgf/cm2

ASTM D 1822

Falling Dart Impact (D 3029), 23°C

1728

cm-kgf

ASTM D 3029

Vicat Softening Temp, Rate B/50

154

°C

ASTM D 1525

HDT, 0.45 MPa, 6.4 mm, unannealed

137

°C

ASTM D 648

HDT, 1.82 MPa, 6.4 mm, unannealed

132

°C

ASTM D 648

CTE, -40°C to 95°C, flow

6.84E-05

1/°C

ASTM E 831

Specific Heat

1.25

J/g-°C

ASTM C 351

Thermal Conductivity

0.19

W/m-°C

ASTM C 177

Relative Temp Index, Elec

125

°C

UL 746B

Relative Temp Index, Mech w/impact

115

°C

UL 746B

Relative Temp Index, Mech w/o impact

125

°C

UL 746B